Material Properties
Comprehensive reference data for common engineering materials. Use filters to narrow results.
| 15-5PH Martensitic precipitation hardenable, H1025 | Stainless Steel | 7,830 | 197 | 1,000 | 1,069 | 1.08e-5 | |
| 15-5PH Martensitic precipitation hardenable, H1150 | Stainless Steel | 7,830 | 197 | 724 | 931 | 1.08e-5 | |
| 15-5PH Martensitic precipitation hardenable, H900 | Stainless Steel | 7,830 | 197 | 1,172 | 1,310 | 1.08e-5 | |
| 17-4PH Martensitic precipitation hardenable, H1025 | Stainless Steel | 7,800 | 197 | 1,000 | 1,069 | 1.12e-5 | |
| 17-4PH Martensitic precipitation hardenable, H1150 | Stainless Steel | 7,800 | 197 | 724 | 931 | 1.12e-5 | |
| 17-4PH Martensitic precipitation hardenable, H900 | Stainless Steel | 7,800 | 197 | 1,172 | 1,310 | 1.08e-5 | |
| 17-7PH Semiaustenitic precipitation hardenable, TH1050 | Stainless Steel | 7,640 | 200 | 1,034 | 1,220 | 1.12e-5 | |
| A-286 Austenitic precipitation hardenable | Stainless Steel | 7,940 | 201 | 655 | 965 | 1.64e-5 | |
| AISI 201 Austenitic, Annealed | Stainless Steel | 8,000 | 193 | 276 | 517 | 1.60e-5 | |
| AISI 202 Austenitic, Annealed | Stainless Steel | 8,000 | 193 | 276 | 517 | 1.70e-5 | |
| AISI 302 Austenitic, Annealed | Stainless Steel | 8,000 | 193 | 207 | 517 | 1.73e-5 | |
| AISI 304 Austenitic, Annealed | Stainless Steel | 8,000 | 193 | 207 | 517 | 1.73e-5 | |
| AISI 304L Austenitic, Annealed | Stainless Steel | 8,000 | 193 | 172 | 483 | 1.73e-5 | |
| AISI 316 Austenitic, Annealed | Stainless Steel | 8,000 | 193 | 207 | 517 | 1.60e-5 | |
| AISI 316L Austenitic, Annealed | Stainless Steel | 8,000 | 193 | 172 | 483 | 1.60e-5 | |
| AISI 405 Ferritic | Stainless Steel | 7,800 | 200 | 172 | 414 | 1.04e-5 | |
| AISI 410 Martensitic, Annealed | Stainless Steel | 7,800 | 200 | 276 | 483 | 9.90e-6 | |
| AISI 410 Martensitic, Quenched & Tempered | Stainless Steel | 7,800 | 200 | 552 | 689 | 9.90e-6 | |
| AISI 430 Ferritic | Stainless Steel | 7,800 | 200 | 207 | 414 | 1.04e-5 | |
| AISI 446 Ferritic, Annealed | Stainless Steel | 7,800 | 200 | 276 | 448 | 1.04e-5 | |
| Alloy 2205 Duplex Austenitic-Ferritic | Stainless Steel | 7,940 | 197 | 448 | 655 | 1.37e-5 | |
| Ferrallium 255 Duplex Austenitic-Ferritic | Stainless Steel | 7,940 | 197 | 552 | 758 | 1.30e-5 |
15-5PH Martensitic precipitation hardenable, H1025
Density: 7,830 kg/m³
Yield Str: 1,000 MPa
E Modulus: 197 GPa
UTS: 1,069 MPa
15-5PH Martensitic precipitation hardenable, H1150
Density: 7,830 kg/m³
Yield Str: 724 MPa
E Modulus: 197 GPa
UTS: 931 MPa
15-5PH Martensitic precipitation hardenable, H900
Density: 7,830 kg/m³
Yield Str: 1,172 MPa
E Modulus: 197 GPa
UTS: 1,310 MPa
17-4PH Martensitic precipitation hardenable, H1025
Density: 7,800 kg/m³
Yield Str: 1,000 MPa
E Modulus: 197 GPa
UTS: 1,069 MPa
17-4PH Martensitic precipitation hardenable, H1150
Density: 7,800 kg/m³
Yield Str: 724 MPa
E Modulus: 197 GPa
UTS: 931 MPa
17-4PH Martensitic precipitation hardenable, H900
Density: 7,800 kg/m³
Yield Str: 1,172 MPa
E Modulus: 197 GPa
UTS: 1,310 MPa
17-7PH Semiaustenitic precipitation hardenable, TH1050
Density: 7,640 kg/m³
Yield Str: 1,034 MPa
E Modulus: 200 GPa
UTS: 1,220 MPa
A-286 Austenitic precipitation hardenable
Density: 7,940 kg/m³
Yield Str: 655 MPa
E Modulus: 201 GPa
UTS: 965 MPa
AISI 201 Austenitic, Annealed
Density: 8,000 kg/m³
Yield Str: 276 MPa
E Modulus: 193 GPa
UTS: 517 MPa
AISI 202 Austenitic, Annealed
Density: 8,000 kg/m³
Yield Str: 276 MPa
E Modulus: 193 GPa
UTS: 517 MPa
AISI 302 Austenitic, Annealed
Density: 8,000 kg/m³
Yield Str: 207 MPa
E Modulus: 193 GPa
UTS: 517 MPa
AISI 304 Austenitic, Annealed
Density: 8,000 kg/m³
Yield Str: 207 MPa
E Modulus: 193 GPa
UTS: 517 MPa
AISI 304L Austenitic, Annealed
Density: 8,000 kg/m³
Yield Str: 172 MPa
E Modulus: 193 GPa
UTS: 483 MPa
AISI 316 Austenitic, Annealed
Density: 8,000 kg/m³
Yield Str: 207 MPa
E Modulus: 193 GPa
UTS: 517 MPa
AISI 316L Austenitic, Annealed
Density: 8,000 kg/m³
Yield Str: 172 MPa
E Modulus: 193 GPa
UTS: 483 MPa
AISI 405 Ferritic
Density: 7,800 kg/m³
Yield Str: 172 MPa
E Modulus: 200 GPa
UTS: 414 MPa
AISI 410 Martensitic, Annealed
Density: 7,800 kg/m³
Yield Str: 276 MPa
E Modulus: 200 GPa
UTS: 483 MPa
AISI 410 Martensitic, Quenched & Tempered
Density: 7,800 kg/m³
Yield Str: 552 MPa
E Modulus: 200 GPa
UTS: 689 MPa
AISI 430 Ferritic
Density: 7,800 kg/m³
Yield Str: 207 MPa
E Modulus: 200 GPa
UTS: 414 MPa
AISI 446 Ferritic, Annealed
Density: 7,800 kg/m³
Yield Str: 276 MPa
E Modulus: 200 GPa
UTS: 448 MPa
Alloy 2205 Duplex Austenitic-Ferritic
Density: 7,940 kg/m³
Yield Str: 448 MPa
E Modulus: 197 GPa
UTS: 655 MPa
Ferrallium 255 Duplex Austenitic-Ferritic
Density: 7,940 kg/m³
Yield Str: 552 MPa
E Modulus: 197 GPa
UTS: 758 MPa