Material Properties
Comprehensive reference data for common engineering materials. Use filters to narrow results.
| 70/30 Copper-Nickel, Annealed | Copper Alloy | 8,940 | 150 | 124 | 310 | 1.62e-5 | |
| 70/30 Copper-Nickel, Cold Worked | Copper Alloy | 8,940 | 150 | 345 | 448 | 1.62e-5 | |
| 90/10 Copper-Nickel, Annealed | Copper Alloy | 8,940 | 140 | 103 | 262 | 1.73e-5 | |
| 90/10 Copper-Nickel, Cold Worked | Copper Alloy | 8,940 | 140 | 207 | 345 | 1.73e-5 | |
| Aluminum Bronze, Generic | Copper Alloy | 7,450 | 107 | 221 | 586 | 1.69e-5 | |
| Beryllium Copper (C17200), Precipitation Heat Treated | Copper Alloy | 8,250 | 128 | 965 | 1,138 | 1.70e-5 | |
| Beryllium Copper (C17200), Solution Heat Treated | Copper Alloy | 8,250 | 128 | 517 | 586 | 1.70e-5 | |
| Beryllium Copper (UNS C17200), Peak-Aged | Copper Alloy | 8,250 | 128 | 965 | 1,380 | 1.78e-5 | |
| Brass C26000 (70% Cu – 30% Zn), Annealed | Copper Alloy | 8,530 | 117 | N/A | 303 | 1.99e-5 | |
| Brass C46400 (Naval Brass) | Copper Alloy | 8,540 | 100 | 300 | 450 | 1.90e-5 | |
| Copper Alloy C71500 (Cu–Ni–Si) | Copper Alloy | 8,900 | 111 | 410 | 690 | 1.70e-5 | |
| Copper, Annealed (99.9% Cu) | Copper Alloy | 8,920 | 120 | 69 | 210 | 1.76e-5 | |
| Nickel Aluminum Bronze (C63000) | Copper Alloy | 8,400 | 117 | 345 | 620 | 1.95e-5 | |
| Nickel Aluminum Bronze (C63200), Annealed | Copper Alloy | 7,580 | 115 | 234 | 621 | 1.62e-5 | |
| Nickel Aluminum Bronze (C63200), Quench Hardened | Copper Alloy | 7,580 | 115 | 345 | 621 | 1.62e-5 | |
| Nickel Silver (Cu–Ni–Zn, 60/20/20) | Copper Alloy | 8,400 | 110 | 95 | 350 | 1.70e-5 | |
| Oxygen‑Free High Conductivity Copper (OFHC, C10200) | Copper Alloy | 8,930 | 117 | 69 | 210 | 1.68e-5 |
70/30 Copper-Nickel, Annealed
Density: 8,940 kg/m³
Yield Str: 124 MPa
E Modulus: 150 GPa
UTS: 310 MPa
70/30 Copper-Nickel, Cold Worked
Density: 8,940 kg/m³
Yield Str: 345 MPa
E Modulus: 150 GPa
UTS: 448 MPa
90/10 Copper-Nickel, Annealed
Density: 8,940 kg/m³
Yield Str: 103 MPa
E Modulus: 140 GPa
UTS: 262 MPa
90/10 Copper-Nickel, Cold Worked
Density: 8,940 kg/m³
Yield Str: 207 MPa
E Modulus: 140 GPa
UTS: 345 MPa
Aluminum Bronze, Generic
Density: 7,450 kg/m³
Yield Str: 221 MPa
E Modulus: 107 GPa
UTS: 586 MPa
Beryllium Copper (C17200), Precipitation Heat Treated
Density: 8,250 kg/m³
Yield Str: 965 MPa
E Modulus: 128 GPa
UTS: 1,138 MPa
Beryllium Copper (C17200), Solution Heat Treated
Density: 8,250 kg/m³
Yield Str: 517 MPa
E Modulus: 128 GPa
UTS: 586 MPa
Beryllium Copper (UNS C17200), Peak-Aged
Density: 8,250 kg/m³
Yield Str: 965 MPa
E Modulus: 128 GPa
UTS: 1,380 MPa
Brass C26000 (70% Cu – 30% Zn), Annealed
Density: 8,530 kg/m³
Yield Str: N/A MPa
E Modulus: 117 GPa
UTS: 303 MPa
Brass C46400 (Naval Brass)
Density: 8,540 kg/m³
Yield Str: 300 MPa
E Modulus: 100 GPa
UTS: 450 MPa
Copper Alloy C71500 (Cu–Ni–Si)
Density: 8,900 kg/m³
Yield Str: 410 MPa
E Modulus: 111 GPa
UTS: 690 MPa
Copper, Annealed (99.9% Cu)
Density: 8,920 kg/m³
Yield Str: 69 MPa
E Modulus: 120 GPa
UTS: 210 MPa
Nickel Aluminum Bronze (C63000)
Density: 8,400 kg/m³
Yield Str: 345 MPa
E Modulus: 117 GPa
UTS: 620 MPa
Nickel Aluminum Bronze (C63200), Annealed
Density: 7,580 kg/m³
Yield Str: 234 MPa
E Modulus: 115 GPa
UTS: 621 MPa
Nickel Aluminum Bronze (C63200), Quench Hardened
Density: 7,580 kg/m³
Yield Str: 345 MPa
E Modulus: 115 GPa
UTS: 621 MPa
Nickel Silver (Cu–Ni–Zn, 60/20/20)
Density: 8,400 kg/m³
Yield Str: 95 MPa
E Modulus: 110 GPa
UTS: 350 MPa
Oxygen‑Free High Conductivity Copper (OFHC, C10200)
Density: 8,930 kg/m³
Yield Str: 69 MPa
E Modulus: 117 GPa
UTS: 210 MPa