Material Properties
Comprehensive reference data for common engineering materials. Use filters to narrow results.
| CFRP (Carbon Fiber/Epoxy) Unidirectional, 55% Fiber | Composite | 1,600 | 140 | N/A | 1,500 | -1.00e-6 | |
| CFRP Quasi-isotropic (0/±45/90, 55% HM Carbon, Epoxy) | Composite | 1,661 | 69 | 758 | 827 | 3.00e-6 | |
| CFRP Unidirectional (0°, 60% HM Carbon, Epoxy) | Composite | 1,605 | 138 | 1,517 | 1,517 | 5.00e-7 | |
| Concrete, Normal Strength (30 MPa) | Composite | 2,400 | 30 | N/A | 4 | 1.00e-5 | |
| FR-4 Fiberglass/Epoxy Laminate | Composite | 1,900 | 22 | N/A | 310 | 1.40e-5 | |
| GFRP Quasi-isotropic (0/±45/90, 50% E-Glass, Vinyl Ester) | Composite | 1,799 | 45 | 414 | 483 | 1.00e-5 | |
| GFRP Unidirectional (0°, 55% E-Glass, Polyester/Epoxy) | Composite | 1,799 | 48 | 552 | 552 | 6.00e-6 | |
| High-Strength Concrete (50 MPa) | Composite | 2,400 | 35 | N/A | 5.2 | 1.00e-5 | |
| Hybrid Carbon/Glass Composite (Alternating, 55%, Epoxy) | Composite | 1,661 | 103 | 1,034 | 1,103 | 4.00e-6 | |
| Kevlar 49/Epoxy Unidirectional Composite | Composite | 1,560 | 80 | N/A | 1,400 | -2.00e-6 | |
| Kevlar Composite Unidirectional (0°, 55% Kevlar, Epoxy) | Composite | 1,439 | 34 | 689 | 689 | -4.00e-6 | |
| Structural Softwood (Pine/Douglas Fir Wood) | Composite | 480 | 12 | N/A | 85 | 5.00e-6 | |
| Ultra‑High Performance Concrete (UHPC) | Composite | 2,400 | 40 | N/A | 8 | 1.00e-5 | |
| Vinyl Ester SMC | Composite | 1,490 | 14 | N/A | 428.65 | 2.50e-5 |
CFRP (Carbon Fiber/Epoxy) Unidirectional, 55% Fiber
Density: 1,600 kg/m³
Yield Str: N/A MPa
E Modulus: 140 GPa
UTS: 1,500 MPa
CFRP Quasi-isotropic (0/±45/90, 55% HM Carbon, Epoxy)
Density: 1,661 kg/m³
Yield Str: 758 MPa
E Modulus: 69 GPa
UTS: 827 MPa
CFRP Unidirectional (0°, 60% HM Carbon, Epoxy)
Density: 1,605 kg/m³
Yield Str: 1,517 MPa
E Modulus: 138 GPa
UTS: 1,517 MPa
Concrete, Normal Strength (30 MPa)
Density: 2,400 kg/m³
Yield Str: N/A MPa
E Modulus: 30 GPa
UTS: 4 MPa
FR-4 Fiberglass/Epoxy Laminate
Density: 1,900 kg/m³
Yield Str: N/A MPa
E Modulus: 22 GPa
UTS: 310 MPa
GFRP Quasi-isotropic (0/±45/90, 50% E-Glass, Vinyl Ester)
Density: 1,799 kg/m³
Yield Str: 414 MPa
E Modulus: 45 GPa
UTS: 483 MPa
GFRP Unidirectional (0°, 55% E-Glass, Polyester/Epoxy)
Density: 1,799 kg/m³
Yield Str: 552 MPa
E Modulus: 48 GPa
UTS: 552 MPa
High-Strength Concrete (50 MPa)
Density: 2,400 kg/m³
Yield Str: N/A MPa
E Modulus: 35 GPa
UTS: 5.2 MPa
Hybrid Carbon/Glass Composite (Alternating, 55%, Epoxy)
Density: 1,661 kg/m³
Yield Str: 1,034 MPa
E Modulus: 103 GPa
UTS: 1,103 MPa
Kevlar 49/Epoxy Unidirectional Composite
Density: 1,560 kg/m³
Yield Str: N/A MPa
E Modulus: 80 GPa
UTS: 1,400 MPa
Kevlar Composite Unidirectional (0°, 55% Kevlar, Epoxy)
Density: 1,439 kg/m³
Yield Str: 689 MPa
E Modulus: 34 GPa
UTS: 689 MPa
Structural Softwood (Pine/Douglas Fir Wood)
Density: 480 kg/m³
Yield Str: N/A MPa
E Modulus: 12 GPa
UTS: 85 MPa
Ultra‑High Performance Concrete (UHPC)
Density: 2,400 kg/m³
Yield Str: N/A MPa
E Modulus: 40 GPa
UTS: 8 MPa
Vinyl Ester SMC
Density: 1,490 kg/m³
Yield Str: N/A MPa
E Modulus: 14 GPa
UTS: 428.65 MPa