Material Properties
Comprehensive reference data for common engineering materials. Use filters to narrow results.
| Alumina Porcelain | Ceramic | 3,500 | 231 | N/A | 131 | 6.80e-6 | |
| Aluminum Nitride (AlN, Dense) | Ceramic | 3,260 | 330 | N/A | 300 | 4.50e-6 | |
| Boron Carbide (B₄C) | Ceramic | 2,520 | 450 | N/A | 200 | 5.00e-6 | |
| Borosilicate Glass (Pyrex) | Ceramic | 2,230 | 64 | N/A | 35 | 3.30e-6 | |
| Cordierite (2MgO·2Al₂O₃·5SiO₂), Dense | Ceramic | 2,600 | 170 | N/A | 30 | 2.00e-6 | |
| Fused Silica (Amorphous SiO₂) | Ceramic | 2,200 | 72 | N/A | 50 | 5.50e-7 | |
| Graphite (Isotropic Carbon) | Ceramic | 1,800 | 11 | N/A | 20 | 4.50e-6 | |
| High-Voltage Porcelain | Ceramic | 2,400 | 72.4 | N/A | 37.9 | 5.90e-6 | |
| Mullite (3Al₂O₃·2SiO₂), Dense | Ceramic | 3,100 | 250 | N/A | 30 | 5.00e-6 | |
| Porcelain | Ceramic | 2,300 | 58.6 | N/A | 13.8 | 5.75e-6 | |
| PZT‑5H (Lead Zirconate Titanate) | Ceramic | 7,700 | 60 | N/A | 100 | 3.00e-6 | |
| Silicon (Monocrystalline, <100>) | Ceramic | 2,330 | 130 | N/A | 700 | 2.60e-6 | |
| Silicon Carbide (SiC) | Ceramic | 3,210 | 410 | N/A | 300 | 4.00e-6 | |
| Silicon Nitride (Si₃N₄), Sintered | Ceramic | 3,250 | 300 | N/A | 300 | 3.20e-6 | |
| Soda–Lime Glass (Annealed) | Ceramic | 2,400 | 71 | N/A | 41 | 8.80e-6 | |
| Titanium Carbide (TiC) | Ceramic | 4,960 | 440 | N/A | 500 | 7.40e-6 | |
| Tungsten Carbide (94% WC – 6% Co) | Ceramic | 15,300 | 600 | N/A | 1,800 | 5.50e-6 | |
| Zirconia Porcelain | Ceramic | 3,650 | 172 | N/A | 86.2 | 4.50e-6 |
Alumina Porcelain
Density: 3,500 kg/m³
Yield Str: N/A MPa
E Modulus: 231 GPa
UTS: 131 MPa
Aluminum Nitride (AlN, Dense)
Density: 3,260 kg/m³
Yield Str: N/A MPa
E Modulus: 330 GPa
UTS: 300 MPa
Boron Carbide (B₄C)
Density: 2,520 kg/m³
Yield Str: N/A MPa
E Modulus: 450 GPa
UTS: 200 MPa
Borosilicate Glass (Pyrex)
Density: 2,230 kg/m³
Yield Str: N/A MPa
E Modulus: 64 GPa
UTS: 35 MPa
Cordierite (2MgO·2Al₂O₃·5SiO₂), Dense
Density: 2,600 kg/m³
Yield Str: N/A MPa
E Modulus: 170 GPa
UTS: 30 MPa
Fused Silica (Amorphous SiO₂)
Density: 2,200 kg/m³
Yield Str: N/A MPa
E Modulus: 72 GPa
UTS: 50 MPa
Graphite (Isotropic Carbon)
Density: 1,800 kg/m³
Yield Str: N/A MPa
E Modulus: 11 GPa
UTS: 20 MPa
High-Voltage Porcelain
Density: 2,400 kg/m³
Yield Str: N/A MPa
E Modulus: 72.4 GPa
UTS: 37.9 MPa
Mullite (3Al₂O₃·2SiO₂), Dense
Density: 3,100 kg/m³
Yield Str: N/A MPa
E Modulus: 250 GPa
UTS: 30 MPa
Porcelain
Density: 2,300 kg/m³
Yield Str: N/A MPa
E Modulus: 58.6 GPa
UTS: 13.8 MPa
PZT‑5H (Lead Zirconate Titanate)
Density: 7,700 kg/m³
Yield Str: N/A MPa
E Modulus: 60 GPa
UTS: 100 MPa
Silicon (Monocrystalline, <100>)
Density: 2,330 kg/m³
Yield Str: N/A MPa
E Modulus: 130 GPa
UTS: 700 MPa
Silicon Carbide (SiC)
Density: 3,210 kg/m³
Yield Str: N/A MPa
E Modulus: 410 GPa
UTS: 300 MPa
Silicon Nitride (Si₃N₄), Sintered
Density: 3,250 kg/m³
Yield Str: N/A MPa
E Modulus: 300 GPa
UTS: 300 MPa
Soda–Lime Glass (Annealed)
Density: 2,400 kg/m³
Yield Str: N/A MPa
E Modulus: 71 GPa
UTS: 41 MPa
Titanium Carbide (TiC)
Density: 4,960 kg/m³
Yield Str: N/A MPa
E Modulus: 440 GPa
UTS: 500 MPa
Tungsten Carbide (94% WC – 6% Co)
Density: 15,300 kg/m³
Yield Str: N/A MPa
E Modulus: 600 GPa
UTS: 1,800 MPa
Zirconia Porcelain
Density: 3,650 kg/m³
Yield Str: N/A MPa
E Modulus: 172 GPa
UTS: 86.2 MPa